Page 1 of 3
Results 1 - 24 of 53

G-1382M

Synthetic Blend

Property Method Typical
Congealing Point F/C ASTM D-938 129.2 / 54

G-1387

Blend

Property Method Typical
Congealing Point F/C ASTM D-938 129.2 / 54

G-1388

Blend

Property Method Typical
Congealing Point F/C ASTM D-938 125.6 / 52

G-0632

Fully Refined Paraffin wax

Property Method Typical
Melting Point F/C ASTM D-87 138.9 / 59.4

G-0121

Fully Refined Paraffin wax

Property Method Typical
Melting Point F/C ASTM D-87 127 / 52.8

G-0123

Fully Refined Paraffin wax

Property Method Typical
Melting Point F/C ASTM D-87 138 / 58.7

G-1623

Fully Refined Paraffin wax

Property Method Typical
Melting Point F/C ASTM D-87 141.3 / 60.7

G-0125

Fully Refined Paraffin wax

Property Method Typical
Melting Point F/C ASTM D-87 142.3 / 61.3

G-0124

Fully Refined Paraffin wax

Property Method Typical
Melting Point F/C ASTM D-87 142.3 / 61.3

G-5804

Base Oil 4 CST

Property Method Typical

G-5806

Base Oil 6 CST

Property Method Typical

G-5803

Base Oil #3 cSt

Property Method Typical

G-0150

Micro

Property Method Typical
Melting Point F/C ASTM D-127 162.3 / 72.4

G-0151

Micro

Property Method Typical
Melting Point F/C ASTM D-127 175.5 / 79.7

G-0152

Micro

Property Method Typical
Melting Point F/C ASTM D-127 182 / 83.3

G-3754

Micro

Property Method Typical
Melting Point F/C ASTM D-127 183.2 / 84

G-3753

Micro

Property Method Typical
Melting Point F/C ASTM D-127 188.6 / 87

G-4710

Palm Wax

Property Method Typical
Melting Point F/C AOCS Cc 1-25 137.8 / 58.8

G-4720

RBD Coconut Oil

Property Method Typical
Melting Point F/C AOCS Cc 1-25 80.6 / 27

G-4770

Triple Pressed Stearic Acid

Property Method Typical

G-4772

Triple Pressed Stearic Acid

Property Method Typical

G-4782

Palm Wax

Property Method Typical
Melting Point F/C AOAC 920 156 138.2 / 54

G-4783

Palm Wax Paraffin Blend

Property Method Typical
Melting Point F/C AOCS Cc 1-25 138.2 / 59
Melting Point F/C ASTM D-127 140 / 60

G-4784

Palm Wax Paraffin Blend

Property Method Typical
Melting Point F/C AOCS Cc 1-25 136.4 / 58